| 镀锌紧固件在储存过程中的锈蚀原因分析 |
| |
| 引用本文： | 姜锐,谭振洲,徐欣轶.镀锌紧固件在储存过程中的锈蚀原因分析[J].全面腐蚀控制,2022(2). |
| |
| 作者姓名： | 姜锐 谭振洲 徐欣轶 |
| |
| 作者单位： | 沈阳宝金金属防护技术有限公司;沈阳防锈包装材料有限责任公司 |
| |
| 摘 要： | 防抱死制动系统(ABS:Anti-lock Braking System)的镀锌紧固件在存储过程中发生锈蚀。分别从大气腐蚀影响因素、腐蚀形貌及能谱分析(EDS)等方面分析了镀锌紧固件的锈蚀原因,并提出合理化建议,避免再次发生类似的锈蚀问题。
|
| 关 键 词： | 镀锌紧固件 大气腐蚀 温度 相对湿度 |
Cause Analysis of Galvanized Fastener Corrosion during Storage |
| |
| JIANG Rui,TAN Zhen-zhou,XU Xin-yi.Cause Analysis of Galvanized Fastener Corrosion during Storage[J].Total Corrosion Control,2022(2). |
| |
| Authors: | JIANG Rui TAN Zhen-zhou XU Xin-yi |
| |
| Affiliation: | (Shenyang Baojin Metal Protecting Technology Co.,Ltd.Shenyang 110032,China;Shenyang Rustproof Packaging Material Co.,Ltd.Shenyang 110032,China) |
| |
| Abstract: | Corrosion of galvanized fasteners in anti-lock braking system(ABS)during storage. The causes of galvanized fasteners corrosion were analyzed from influence factors of atmospheric corrosion,corrosion morphology and energy dispersive spectrum analysis(EDS), and rationalization suggests was proposed to avoid similar corrosion problems again. |
| |
| Keywords: | galvanized fasteners atmospheric corrosion temperature relative humidity |