| 宁波钢铁连铸坯热装热送生产实践 |
| |
| 引用本文： | 陈红雨,于长春,张建方. 宁波钢铁连铸坯热装热送生产实践[J]. 山东冶金, 2012, 0(1): 57-58 |
| |
| 作者姓名： | 陈红雨 于长春 张建方 |
| |
| 作者单位： | 宁波钢铁有限公司,浙江宁波315807 |
| |
| 摘 要： | 基于ERP系统的信息管理技术,宁钢实现了高温无缺陷板坯生产,板坯无缺陷率稳定在99%以上。通过加强管理,板坯平均直接热装率达55%,入炉平均温度699℃;间接热装率达75%,入炉平均温度650℃。宁钢实行连铸坯热装热送技术,缩短了生产周期,节约了能源,减少了金属烧损。
|
| 关 键 词： | 连铸坯 热装热送 无缺陷板坯 |
Hot-charging and Hot Direct Charging Practice of Continuously Casting Slabs in Ningbo Steel |
| |
| CHEN Hong-yu,YU Chang-chun,ZHANG Jian-fang. Hot-charging and Hot Direct Charging Practice of Continuously Casting Slabs in Ningbo Steel[J]. Shandong Metallurgy, 2012, 0(1): 57-58 |
| |
| Authors: | CHEN Hong-yu YU Chang-chun ZHANG Jian-fang |
| |
| Affiliation: | (Ningbo Iron and Steel Co., Ltd., Ningbo 315807, China) |
| |
| Abstract: | Based on the information management technique of ERP system, Ningbo Steel realized the slab production of high temperature and no defects. The no defect rate of the slab stabilized at 99% above. Through strengthening management, the average hot direct charging rate of the slabs reached 55%, average charging temperature was 699 ℃; hot charge rolling rate reached 75% and average charging temperature was 650 ℃. The hot-charging and hot direct charging technology shortened production cycle and reduced the metal loss. |
| |
| Keywords: | continuously casting slab hot-charging and hot direct charging no defects slab |