| 退火工艺对Al/Mg/Al复合板界面结合与阻尼性能的影响 |
| |
| 引用本文： | 王敬丰,吴忠山,王少华,杨文翔,马社,潘复生.退火工艺对Al/Mg/Al复合板界面结合与阻尼性能的影响[J].材料导报,2016,30(24):59-65. |
| |
| 作者姓名： | 王敬丰 吴忠山 王少华 杨文翔 马社 潘复生 |
| |
| 作者单位： | 1. 重庆大学材料科学与工程学院，国家镁合金材料工程技术研究中心，重庆 400044;2. 中国工程物理研究院，应用电子学研究所，绵阳 621900 |
| |
| 基金项目： | 国家自然科学基金(51271206);国家重点基础研究发展计划(2013CB632201);中物院高能激光科学与技术实验室基金 |
| |
| 摘 要： | 研究了Al/Mg/Al三明治结构复合板的退火热处理工艺,探讨了退火温度、时间对复合界面和阻尼性能的影响。结果表明:退火使得Mg层中的孪晶及变形组织消失,晶粒明显长大,且可以促进Al-Mg界面原子的相互扩散。随着退火温度的升高,界面效应对复合板的阻尼性能影响由不利转变为有利,在250℃下随着退火时间的延长,复合板的阻尼性能有一定的提高。综合复合板的组织与性能要求,得到Al/Mg/Al复合板的最佳退火工艺为250℃×2h,在应变振幅为5×10~(-4)下复合板的阻尼值Q~(-1)达0.045。
|
| 关 键 词： | Al/Mg/Al复合板 退火工艺 复合界面 阻尼性能 |
Effect of Annealing Process on Compound Interface and Damping Capacity of Al/Mg/Al Composite Sheet |
| |
| WANG Jingfeng,WU Zhongshan,WANG Shaohu,YANG Wenxiang,MA She and PAN Fusheng.Effect of Annealing Process on Compound Interface and Damping Capacity of Al/Mg/Al Composite Sheet[J].Materials Review,2016,30(24):59-65. |
| |
| Authors: | WANG Jingfeng WU Zhongshan WANG Shaohu YANG Wenxiang MA She and PAN Fusheng |
| |
| Affiliation: | National Engineering Research Center for Magnesium Alloys, College of Materials Science and Engineering, Chongqing University, Chongqing 400044,National Engineering Research Center for Magnesium Alloys, College of Materials Science and Engineering, Chongqing University, Chongqing 400044,National Engineering Research Center for Magnesium Alloys, College of Materials Science and Engineering, Chongqing University, Chongqing 400044,National Engineering Research Center for Magnesium Alloys, College of Materials Science and Engineering, Chongqing University, Chongqing 400044,Institute of Applied Electronics, China Academy of Engineering Physics, Mianyang 621900 and National Engineering Research Center for Magnesium Alloys, College of Materials Science and Engineering, Chongqing University, Chongqing 400044 |
| |
| Abstract: | The influences of annealing temperature and time on compound interface and damping capacity of the Al/Mg/Al sandwich composite sheet were investigated in this paper.The results show that twin and deformation mi-crostructure in Mg layer disappeared with the growth of recrystallized grain,and the atoms of Al-Mg interface mutual-ly diffused after annealing treatment.The impacts of interface effect on the damping capacities changes from bad to good with rising annealing temperature.Damping capacities of sheet have a certain improvement with the extension of annealing time at 250 ℃.Furthermore,the optimal annealing technology of the Al/Mg/Al sheet is at 250 ℃ for 2 hours to achieve excellent microstructure and properties,which exhibits high damping capacity of 0.045 at strain am-plitude of 5×10-4 . |
| |
| Keywords: | Al/Mg/Al composite sheet annealing process compound interface damping capacity |