Ba3ZnTa2−xNbxO9 and Ba3MgTa2−xNbxO9 (0≤x≤1): synthesis, structure and dielectric properties

Oxides belonging to the families Ba₃ZnTa_2−xNb_xO₉ and Ba₃MgTa_2−xNb_xO₉ were synthesized by the solid state reaction route. Sintering temperatures of 1300°C led to oxides with disordered (cubic) perovskite structure. However, on sintering at 1425°C hexagonally ordered structures were obtained for Ba₃MgTa_2−xNb_xO₉ over the entire range (0≤x≤1) of composition, while for Ba₃ZnTa_2−xNb_xO₉ the ordered structure exists in a limited range (0≤x≤0.5). The dielectric constant is close to 30 for the Ba₃ZnTa_2−xNb_xO₉ family of oxides while the Mg analogues have lower dielectric constant of ∼18 in the range 50 Hz to 500 kHz. At microwave frequencies (5-7 GHz) dielectric constant increases with increase in niobium concentration (22-26) for Ba₃ZnTa_2−xNb_xO₉; for Ba₃MgTa_2−xNb_xO₉ it varies between 12 and 14. The “Zn” compounds have much higher quality factors and lower temperature coefficient of resonant frequency compared to the “Mg” analogues.