Nano Fe3O4 Induced Fluxoid Jumps and Low Field Enhanced Critical Current Density in MgB2 Superconductor

Nano particle of Fe₃O₄ (nFe₃O₄) up to 6 at% were doped in the superconducting MgB₂ samples. Despite the strong ferromagnetic nature of Fe₃O₄, both the ac susceptibility and the resistivity measurements show that up to 4 at% of Fe₃O₄, T _c =38 K is not changed, whereas for 6% T _c decreases by 6 K. This indicates that a low concentration of Fe does not substitute either the Mg or B sites and probably occupies the intergrain spaces. For 0.5% doped Fe₃O₄, an increase in J _c with respect to the pure MgB₂ samples is observed in the lower field and temperature regions (H<2 T and 20 K) indicating an enhanced flux pinning and the magnetic activation, i.e., the interaction between the magnetic dipole of Fe ion and the vortices is weak in comparison to the effective pinning potential. Whereas, at H>2 T, J _c of the doped samples is always less than that of MgB₂, and the activation is dominant in comparison with the effective pinning potential provided by the doping. Flux jumps are observed in lower T and H regions for the samples doped up to 1% nFe₃O₄ only. Magnetization plots of higher Fe content samples exhibited clear paramagnetic background. Mossbauer measurements for the higher (4, 6 at%) nFe₃O₄ doped MgB₂ samples show that at RT, the hyperfine field for both samples is ∼100 kOe and ∼120 kOe at 90 K. This means that the nFe₃O₄ particles decompose and form possibly an intermetallic Fe-B phase in the matrix.