Rapid Crystallization of SiO2-Al2O3 Glasses

The crystallization of Al₂O₃-rich glasses in the system SiO₂-Al₂O₃ which were prepared by flame-spraying and/or splat-cooling was studied by DTA, electron microscopy, and X-ray diffraction. Over a wide range of compositions, the crystallization temperature ( T_x ) remained near 1000°C, changing smoothly with composition. In all cases crystallization of mullite was detected by X-ray diffraction. In the low-Al₂O₃ region, coarsening of the microstructure during crystallization was observed by electron microscopy. In the high-Al₂O₃ region mullite and γ-Al₂O₃ cocrystallized; this behavior may be interpreted as evidence of a cooperative process of crystallization at the respective T_x 's. The crystallite size of the mullite immediately after rapid crystallization increased continuously with increasing Al₂O₃ content. In light of the T_x data, the adequacy of the evidence for the proposed metastable miscibility gap in the SiO₂-Al₂O₃ system is questioned.