| Abstract: | Corrosion resistant metallic materials for flue gas desulfurization plants Forced by environmental legislation installations for flue gas desulfurization (FGD) are presently being built to a large extent in the Federal Republic of Germany as in some other countries. Absorption by lime/limestone slurries is used in most cases for desulfurization. The components of the flue gas as well as the kind of process applied are of primary importance for the corrosive behaviour of the materials of construction. In view of pH values going down below 1 in some cases, chloride contents of occasionally more than 10% Cl?, temperatures between 40 and 160°C and local deposits of solids it is the resistance to pitting and crevice corrosion which has to be considered in the first place while stress corrosion cracking and erosion corrosion are of minor importance. Therefore, only austenitic materials with molybdenum contents of more than 2 wt.-% have to be considered. According to the severity of the corrosive media these are predominantly alloys as e.g. Cronifer 1925 LCN (Alloy 904 LN), 1925 hMo (Alloy 904 LM) going up to the high alloyed nickel base materials Nicrofer 6020 hMo (Alloy 625) and 5716 hMo W (Alloy C-276), which exhibit molybdenum contents of 9 and 16 wt.-% and are to be used at places where corrosion is extremely severe as e.g. at the raw gas inlet. The use of such high alloyed materials plated on carbon steel has been tried successfully. Special attention has to be paid to all aspects of welding in order to avoid welds to become locations being vulnerable by corrosive attack. Therefore, welding of corrosion resistant materials in FGD units has been investigated extensively. The results of application oriented laboratory tests as well as practical experience with existing FGD units are to be considered. Correct use of corrosion resistant metallic materials will be an important contribution to minimizing repair and shut downs of FGD units and to extend their life. |