两种封端聚醚大单体及其共聚物制备与阻磷酸钙垢应用

采用烯丙基聚乙二醇单醚APEO10为原料制备了大分子单体磺酸盐封端聚醚APES10和羧酸盐封端聚醚APEC10并分别与小分子单体丙烯酸AA聚合生成两种聚羧酸类阻垢剂AA/APES10和AA/APEC10,用红外光谱、核磁共振对其结构进行了表征。实验确定了聚合反应单体最佳质量比为m(APES10):m(AA)=1:1,m(APEC10):m(AA)=2:3。通过静态阻垢实验对比了两种聚合物的阻磷酸钙垢性能。结果表明,合成的两种阻垢剂AA/APES10和AA/APEC10在临界值6 mg·L^-1时阻磷酸钙垢率分别为92%、100%,但羧酸盐封端聚醚大单体合成的阻垢剂AA/APEC10阻磷酸钙垢能力优于磺酸盐封端聚醚大单体合成的阻垢剂,且聚合物AA/APEC10只含碳、氢、氧、钠4种元素,无氮、磷污染,可以充当循环水用环保型阻磷酸钙垢阻垢剂。

Synthesis of capped polyether macromonomers and their copolymers as antiscalants for calcium phosphate

Capped polyether macromonomers APES10 and APEC10 were synthesized from allyl polyethylene glycol sole ether APEO10,and their polycarboxylic acid type copolymers AA/APES10,AA/APEC10 as antiscalants were prepared from small molecule monomers acrylic acid AA.The products were characterized by FT-IR and ¹H NMR and the performance of their copolymers of calcium phosphate inhibition was evaluated by the static scale-inhibiting method.The studies indicated that when mass ratio of APES10 to AA was 1:1,APEC10 to AA was 2:3,both AA/APEC10 and AA/APES10 had much better ability to inhibit the precipitation of calcium phosphate than other mass ratios.It was also shown that both AA/APEC10 and AA/APES10 had superior ability to inhibit the precipitation of calcium phosphate when the dosage was 6 mg·L^-1,approximately showing 100%,92% inhibition,respectively. While compared to that of AA/APES10,AA/APEC10 had superior ability to control calcium-phosphate deposition.Furthermore,the synthesized AA/APEC10 is an environmentally friendly antiscalant,only containing four elements of carbon (C),hydrogen (H),oxygen (O),sodium (Na),without phosphorous (P)and nitrogen (N).AA/APEC10 is an excellent performance non-phosphorus inhibitor for calcium phosphate scaling in industrial recycling water systems.