Influence of different coating structures on the oxidation resistance of MoSi2 coatings

Two different structures of MoSi₂ coatings were prepared on Niobium based alloys by using a two step process. The as-deposited type(a) MoSi₂ coating structure consists of a MoSi₂ layer on the surface and a NbSi₂ layer underneath, while the type(b) MoSi₂ coating consists of an outer MoSi₂ layer and an inner unsiliconized Mo layer. The oxidation behaviors of the two different types MoSi₂ coatings were examined at 1200 °C for 100 h in air, and the mass gains of type(a) and type(b) MoSi₂ coated specimens were 0.64 mg/cm² and 0.59 mg/cm² respectively. The excellent oxidation resistance of both type(a) and type(b) MoSi₂ coated samples at 1200 °C was due to the formation of a dense and continuous SiO₂ scale during oxidation. As the CTE mismatch between the outer MoSi₂ coating and the inner layer, cracks distributed within both type(a) and type(b) MoSi₂ coating structures.