Doping of Nb to the Ba and Cu Sites in the Y0.6Gd0.4Ba2Cu3O7−δ |
| |
Authors: | M Yılmaz E Sönmez O Doğan |
| |
Affiliation: | 1. Department of Physics, A. Kele?o?lu Education Faculty, Sel?uk University, 42099, Meram-Konya, Turkey 2. Department of Physics, K.K. Education Faculty, Ataturk University, 25240, Yakutiye-Erzurum, Turkey 3. Advanced Materials Research Laboratory, Department of Nanoscience & Nanoengineering, Graduate School of Natural and Applied Sciences, Atatürk University, 25240, Erzurum, Turkey
|
| |
Abstract: | Polycrystalline samples of Y0.6Gd0.4Ba2?x Nb x Cu3O7?δ and Y0.6Gd0.4Ba2Cu3?x Nb x O7?δ with different Nb contents (x=0.025, 0.075, 0.125, 0.175 and 0.225) were prepared using the solid state reaction method. Structural and electrical properties of new compounds were investigated with optical microscope, scanning electron microscopy (SEM), X-ray diffraction (XRD), Four Point Probe (FPP). The results indicated that Nb constituted YBa2NbO6 structure instead of substituting to the Y0.6Gd0.4Ba2Cu3O7?δ structure. YBa2NbO6 structures gathered between grains. Transition temperature did not change significantly, but critical current (J c) values decreased with increase of Nb concentration. The underlying reason is that the oxygen concentration of compounds remained unchanged due to Gd; thus, T c values did not change significantly. |
| |
Keywords: | |
本文献已被 SpringerLink 等数据库收录! |
|