In situ crack growth observation and fracture toughness measurement of hydrogen charged Zircaloy-4

The effect of hydrogen on the fracture behaviour of a Zircaloy-4 alloy was analysed performing simultaneous fracture mechanics tests of small SE(B) specimens and in situ observation of crack initiation and propagation inside the chamber of a scanning electron microscope. Load and displacement were continuously measured and J_IC, J-R curves and CTOD determinations were obtained. Detailed images of the zone close to the crack tip were taken and the resistance to crack growth was correlated with hydrogen content and hydride morphology. The size and orientation of hydride precipitates showed an important influence on the fracture process. A good agreement with results obtained using standard CT specimens was met.