| Abstract: | Fuel rod failure behavior has been studied under a reactivity initiated accident condition in Nuclear Safety Research Reactor (NSRR), JAERI. In the studies, inetallurgical observations showed that the incipient fuel rod failure mode was oxygen-induced embrittlement of the cladding independent of the test conditions such as fuel designs and cooling environments except for pressurized and waterlogged fuels. Development of the oxidation layers and embrittlement of β-Zry were quantitatively evaluated through the metallurgical examinations. A diffusion equation of oxygen was solved under a finite system with moving boundary conditions to obtain the oxygen concentration and evaluate the cladding embrittlement. The calculation showed that the wall thinning due to the cladding melt is needed for the complete embrittlement because the wall thinning enhances the oxygen concentration in the β-Zry, which well explain the experimental results. Therefore the failure threshold energy is determined by the cladding melting temperature. The failure threshold derived from this study is expected to be applicable to predicting the fuel rod failure behavior in computer analyses and also useful to evaluate the failure threshold energy for the new types of fuel rod. |