| Abstract: | In-pile release of fission gas from sintered UC pellets in the presence of 8–230 ppm of water vapor in the He sweep gas was measured over the temperature range of 160°–1,000°C. A very complex release behavior was observed and the mechanisms of release were deduced from the manner in which the release depended on the decay constant. It was established that the release of short-lived fission gases during irradiation was controlled mainly by pseudo-recoil, while chemical reaction between UC and water vapor, as well as knock-out, appeared to contribute much more significantly in the case of the longer-lived fission gases. The release of fission gas after reactor shutdown was shown to be governed by the UC-H2O reaction. The ratio of the release due to this reaction in reference to the total release was found to be dependent not only on the concentration of the water vapor but also on the amount present of the accumulated reaction products. Also, a discussion is given on the inordinately high release of 135mXe observed at 600°C. |