| Abstract: | In order to investigate irradiation effects on nodular corrosion resistance of Zircaloy-4, an out-of-pile corrosion test was conducted using Zircaloy-4 specimens cut from the channel box of a fuel assembly irradiated in the BWR (Monticello reactor) up to the neutron fluence of 1.53×1026 n/m2 (E>1MeV). The corrosion test was carried out in high pressure steam of 10.3 MPa at 783 K for 24 h. No nodules appeared on the specimens cut from welded areas of the channel box and nodular corrosion resistance tended to be better with increasing neutron fluence. Microstructural evolution in the form of irradiation-induced release of Fe atoms from Zr(Fe, Cr)2 type precipitates was detected by an analytical electron microscope. It was found that the higher the concentration of dissolved Fe and Cr in the grains of Zircaloy-4, the better the nodular corrosion resistance. |