Self-flux synthesis and photoluminescent properties of LiAl5O8

Pure-phase LiAl₅O₈ was selected as an oxide ceramic red phosphor material without dopants (color centers) and was synthesized using a self-flux method. The LiAl₅O₈ was formed by heating a powder mixture consisting of γ-Al₂O₃:Li₂SO₄ = 1:2 (molar ratio) at over 1100 °C for 1 h. Photoluminescence (PL) properties for the synthesized LiAl₅O₈ were investigated. The maximum intensity of the excitation spectrum for the photoluminescent emission of LiAl₅O₈ synthesized was at 274 nm. The peak intensity of the emission spectrum was at a wavelength of 667 nm (red color). The intensity of the peak emission spectrum increased with the heating temperature, i.e., the maximum peak intensity of the red emission spectrum was detected for the LiAl₅O₈ synthesized by heating at 1500 °C for 1 h.