| 铸件侵入性气孔的产生原因及防止措施 |
| |
| 引用本文： | 郭续利. 铸件侵入性气孔的产生原因及防止措施[J]. 机械管理开发, 2001, 0(1): 52-52 |
| |
| 作者姓名： | 郭续利 |
| |
| 作者单位： | 山西建筑机械厂,030024 |
| |
| 摘 要： | 气孔是铸造生产中最常见的铸件缺陷之一，铸件废品中占有很大比例的是由于气孔，尤其以便入性气孔为最多，减少和消除气孔缺陷对提高铸件质量是十分迫切的问题。
|
| 关 键 词： | 铸件 侵入性气孔 铸造缺陷 质量 |
| 文章编号： | 1003-773X(2001)01-0052-01 |
| 修稿时间： | 2000-12-18 |
Reason and Prevention of Irruptive Gas Holes in Cast Parts |
| |
| Guo Xuli. Reason and Prevention of Irruptive Gas Holes in Cast Parts[J]. Mechanical Management and Development, 2001, 0(1): 52-52 |
| |
| Authors: | Guo Xuli |
| |
| Abstract: | Gas holes are especially one of the most common defects in cas t p roducts and the main reason for the most of the waste products, so reducing a nd eliminating gas holes are the key to improving the quality of cast products. |
| |
| Keywords: | Cast part Irruptive gas Hole |