Examination of the fatigue crack growth equations |
| |
Authors: | R. S. Li A. Chudnovsky |
| |
Affiliation: | (1) Automotive and Industrial Electronics Group, Motorola Inc., 4000 Commercial Ave., 60062 Northbrook, IL, USA;(2) Department of Civil Engineering and Materials Engineering, The University of Illinois at Chicago, 842 W. Taylor St., 60607 Chicago, IL, USA |
| |
Abstract: | Most of the crack growth equations proposed so far correlate the crack growth rate (da/dN or da/dt) with crack tip parameters such as the stress intensity factor (SIF) or energy release rate (ERR). In our previous works, an experimental setup was designed to examine the applicability and the boundary of the functional relationship between da/dN and the crack tip parameters, particularly, ERR. In the present paper, the variation of the ERR along the experimentally observed curvilinear crack trajectories is obtained by means of the finite element method. The analysis shows that the Paris-Erdogan type of laws are applicable until the crack tip is located outside the strong crack-defect interaction region (SI region). A functional relationship between da/dN and ERR breaks down within this region. This suggests the existence of additional crack tip parameters that are not accounted for within conventional fracture mechanics. An approach to modeling the observed phenomenon is discussed following the concept of the Crack Layer theory. |
| |
Keywords: | fatigue crack growth crack damage interaction |
本文献已被 SpringerLink 等数据库收录! |
|