and R-curve fracture toughness values for aluminum alloys under plane stress conditions |
| |
Authors: | DL Jones PK Poulose J Eftis H Liebowitz |
| |
Affiliation: | School of Engineering and Applied Science, The George Washington University, Washington, DC 20052, U.S.A. |
| |
Abstract: | The effect of specimen geometry and subcritical crack growth on the nonlinear energy fracture toughness, , has been examined for thin, center-cracked sheets of 2024-T3 and 7075-T6 aluminum alloys. The procedure followed was to independently vary the specimen length, L, width, w, andd crack length-to-specimen width ratio and to determine the toughness both at the onset of subcritical crack growth and at the initiation of unstable fracture. Comparisons were also made with the R-curve toughness, GR, evaluated at unstable fracture from which it was found that both and GR displayed the same trend of change with geometrical variables, with consistently higher than GR. When the nonlinear energy fracture toughness was evaluated at the onset of subcritical crack growth, it was found that the geometry dependence essentially disappeared.Scanning electron microscopic examination of some typical fracture surfaces showed that stable crack growth was accompanied by a gradual change of fracture mode from plane strain to plane stress. An analysis of possible errors in the experimental procedure showed that the scatter observed in values was not due to experimental errors, but apparently due to inhomogeneities in the materials. Several techniques were also introduced for the purpose of more directly incorporating crack growth into the determination, but it was found that they did not cause significant variation in the toughness values. |
| |
Keywords: | |
本文献已被 ScienceDirect 等数据库收录! |
|