| 20g钢在单乙醇胺富液中应力腐蚀敏感性研究 | |
| 引用本文： | 段小林,方德明,陈冰冰,巫少龙,章秋香.20g钢在单乙醇胺富液中应力腐蚀敏感性研究[J].全面腐蚀控制,2003,17(6):7-9. |
| 作者姓名： | 段小林 方德明 陈冰冰 巫少龙 章秋香 |
| 作者单位： | 1. 浙江工业大学,过程装备与控制研究所,浙江,杭州,310032 2. 浙江工业大学,浙西分校,浙江,衢州,324006 3. 温州市工业设计院,浙江,温州,325003 |
| 摘 要： | 通过慢拉伸应力腐蚀试验,研究了20g钢在单乙醇胺富液中的应力腐蚀行为,结果表明,20g在单乙醇胺富液中,对应力腐蚀敏感性不大,高温时敏感性指数比常温时高。 |
| 关 键 词： | 应力腐蚀 20g钢 敏感性 单乙醇胺富液 |
Study on SCC Sensitivity of 20g Steel in MEA Rich Solution |
|
| Duan Xiaolin,Fang Deming,Chen Bingbing,Wu Shaolong,Zhang Qiuxiang.Study on SCC Sensitivity of 20g Steel in MEA Rich Solution[J].Total Corrosion Control,2003,17(6):7-9. | |
| Authors: | Duan Xiaolin Fang Deming Chen Bingbing Wu Shaolong Zhang Qiuxiang |
| Affiliation: | Duan Xiaolin1,Fang Deming1,Chen Bingbing1,Wu Shaolong2,Zhang Qiuxiang3 |
| Abstract: | The stress corrosion behavior of 20g steel in MEA rich solution was studied through the slow strain rate test. Theresults show that the SCC sensitivity of 20g steel in MEA rich solution is low, but it is relative higher when the test temperature israised. |
| Keywords: | stress corrosion cracking 20g steel sensitivity MEA rich solution |