| 温度对碱-磷渣水泥水化的影响 |
| |
| 引用本文： | 史才军. 温度对碱-磷渣水泥水化的影响[J]. 陶瓷科学与艺术, 1989, 0(1) |
| |
| 作者姓名： | 史才军 |
| |
| 作者单位： | 南京化工学院硅酸盐工程系 |
| |
| 摘 要： | 本文研究了两种碱-磷渣水泥(用NaOH作为碱性激发剂的MO及用Na_2O·SiO_2作为碱性激发剂的M_1)在不同温度下的水化放热速率及强度发展情况。实验结果表明,M1水泥对温度的敏感性高于M0水泥,原因是这两种水泥的表现水化活化能不一样,M0水泥的为38.89KJ/mol,而M1水泥的为64.62KJ/mol。
|
| 关 键 词： | 温度 碱—磷渣水泥 水化 表观水化活化能 |
EFFECT OF TEMPERATURE ON HYDRATION OF ALKALI-PHOSPHORUS SLAG CEMENT |
| |
| Shi Caijun. EFFECT OF TEMPERATURE ON HYDRATION OF ALKALI-PHOSPHORUS SLAG CEMENT[J]. Ceramics Science & Art, 1989, 0(1) |
| |
| Authors: | Shi Caijun |
| |
| Affiliation: | Department of Silicate Engineering |
| |
| Abstract: | The hydration heat evolution rates and the strength developments of two kinds of alkali-phosphorus slag cement (sample Mo activated by NaOH and Ml activated by Na_2 O.SiO_2) at different temperature were studied. The experimental results showed that the influence of temperature on the hydration of Ml was greater than that of Mo, as Ml had a higher apparent activation energy. The apparent activation energy for Mo and Ml were 38.39 and 64.62 KJ/mol respectively. |
| |
| Keywords: | temperature alkali-phosphorus slag cement hydration apparent activation energy |