Performance of LiNi1/3Co1/3Mn1/3O2 prepared from spent lithium-ion batteries by a carbonate co-precipitation method

Spherical LiNi_1/3Co_1/3Mn_1/3O₂ cathode particles were resynthesized by a carbonate co-precipitation method using spent lithium-ion batteries (LIBs) as a raw material. The physical characteristics of the Ni_1/3Co_1/3Mn_1/3CO₃ precursor, the (Ni_1/3Co_1/3Mn_1/3)₃O₄ intermediate, and the regenerated LiNi_1/3Co_1/3Mn_1/3O₂ cathode material were investigated by laser particle-size analysis, scanning electron microscopy–energy-dispersive spectroscopy (SEM-EDS), thermogravimetry–differential scanning calorimetry (TG-DSC), X-ray diffraction (XRD), inductively coupled plasma–atomic emission spectroscopy (ICP-AES), and X-ray photoelectron spectroscopy (XPS). The electrochemical performance of the regenerated LiNi_1/3Co_1/3Mn_1/3O₂ was studied by continuous charge–discharge cycling and cyclic voltammetry. The results indicate that the regenerated Ni_1/3Co_1/3Mn_1/3CO₃ precursor comprises uniform spherical particles with a narrow particle-size distribution. The regenerated LiNi_1/3Co_1/3Mn_1/3O₂ comprises spherical particles similar to those of the Ni_1/3Co_1/3Mn_1/3CO₃ precursor, but with a narrower particle-size distribution. Moreover, it has a well-ordered layered structure and a low degree of cation mixing. The regenerated LiNi_1/3Co_1/3Mn_1/3O₂ shows an initial discharge capacity of 163.5 mA h g^?1 at 0.1 C, between 2.7 and 4.3 V; the discharge capacity at 1 C is 135.1 mA h g^?1, and the capacity retention ratio is 94.1% after 50 cycles. Even at the high rate of 5 C, LiNi_1/3Co_1/3Mn_1/3O₂ delivers the high capacity of 112.6 mA h g^?1. These results demonstrate that the electrochemical performance of the regenerated LiNi_1/3Co_1/3Mn_1/3O₂ is comparable to that of a cathode synthesized from fresh materials by carbonate co-precipitation.