| Microstructures and Corrosion Resistance of Al2O3—C Based Refractories to the Melts Containing Titania |
| |
| 引用本文： | LIUQingai W.Newkirk 等.Microstructures and Corrosion Resistance of Al2O3—C Based Refractories to the Melts Containing Titania[J].中国耐火材料,2002,11(1):3-8. |
| |
| 作者姓名： | LIUQingai W.Newkirk |
| |
| 作者单位： | [1]CollegeofMaterialsScienceandEngineering,ChongqingUniversityChongqing,P.R.China400044 [2]DepartmentofMetallurgicalEngineering,UniversityofMissouri－RollaRolla,MO65409,USA |
| |
| 摘 要： | The corrosion resisance of the Al2O3-C based refrac-tories in melts containing titania has been studied by quasi-station immersion and rotary immersionThe corrosion rate is decreased with the addition of graphite carbon and ZrO2 in the refractories.The corrosion mehanism of Al2O3-C refractories is the oxidization of graphite carbon by the oxides of the melts and the formation of deteriorate layer,For the Al2O3-C-ZrO2 refractories,the corrosion behavior is due to the interaction between melts and refrac-tories,The new compounds of FeO.SiO2,SiZrO4,Feo.3CaO,2CaO.SiO2 and CaO.SiO2 are formed in the deteriorate layer.
|
| 关 键 词： | 微观结构 耐腐蚀能力 三氧化二铝 碳 Al2O3 C 耐火材料 熔化物 二氧化钛 Ti |
Microstructures and Corrosion Resistance of Al2O3-C Based Refractories to the Melts Containing Titania |
| |
| Liu Qingcai,XU Yuan,Chen Dengfu,OU Yangqi,Joseph W.Newkirk.Microstructures and Corrosion Resistance of Al2O3-C Based Refractories to the Melts Containing Titania[J].China’s Refractories,2002,11(1):3-8. |
| |
| Authors: | Liu Qingcai XU Yuan Chen Dengfu OU Yangqi Joseph WNewkirk |
| |
| Abstract: | The corrosion resistance of the Al2O3-C based refractories in melts containing titania has been studied by quasi-station immersion and rotary immersion. The corrosion
rate is decreased with the addition of graphite carbon, and ZrO2 in the refractories . The corrosion, mechanism of Al2O3-C refractories, is. the oxidization of graphite carbon by the oxides of the melts the formation of deteriorate layer, For the Al2O3-C-ZrO2 refractories, the corrosion behavior is due to the, interaction between melts and refractories . The new compounds of FeO. SiO2, SiZrO4, FeO. 3 CaO, 2CaO. SiO2 and CaO. SiO2 are formed in the deteriorate layer. |
| |
| Keywords: | Melts Alumina-carbon based refractory Immersion test Corrosion resistance |