Formation of LiNi0.5Co0.5VO4 nano-crystals by solvothermal reaction

LiNi_0.5Co_0.5VO₄ nano-crystals were solvothermally prepared using a mixture of LiOH·H₂O, Ni(NO₃)₂·6H₂O, Co(NO₃)₂·6H₂O and NH₄VO₃ in isopropanol at 150–200 °C followed by 300–600 °C calcination to form powders. TGA curves of the solvothermal products show weight losses due to evaporation and decomposition processes. The purified products seem to form at 500 °C and above. The products analyzed by XRD, selected area electron diffraction (SAED), energy dispersive X-ray (EDX) and atomic absorption spectrophotometer (AAS) correspond to LiNi_0.5Co_0.5VO₄. V–O stretching vibrations of VO₄ tetrahedrons analyzed using FTIR and Raman spectrometer are in the range of 620–900 cm⁻¹. A solvothermal reaction at 150 °C for 10 h followed by calcination at 600 °C for 6 h yields crystals with lattice parameter of 0.8252 ± 0.0008 nm. Transmission electron microscope (TEM) images clearly show that the solvothermal temperatures play a more important role in the size formation than the reaction times.