Affiliation: | 1. CAS Key Laboratory of Nuclear Materials and Safety Assessment, Institute of Metal Research, Chinese Academy of Sciences, Shenyang, 110016 China Shi-changxu Innovation Center for Advanced Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang, 110016 China School of Materials Science and Engineering, University of Science and Technology of China, Hefei, 230026 China;2. CAS Key Laboratory of Nuclear Materials and Safety Assessment, Institute of Metal Research, Chinese Academy of Sciences, Shenyang, 110016 China;3. CAS Key Laboratory of Nuclear Materials and Safety Assessment, Institute of Metal Research, Chinese Academy of Sciences, Shenyang, 110016 China Shi-changxu Innovation Center for Advanced Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang, 110016 China |
Abstract: | Herein, the effects of Fe/Ni ratio on the microstructure, mechanical properties, and corrosion resistance in a 3.5 wt% NaCl solution of FexNi65−xCr20Al10Nb5 are investigated systematically. It is found that the phases shifted from the FCC-dominated to the BCC-dominated with the molar ratio of the Fe/Ni increased. The strength of FexNi65−xCr20Al10Nb5 increases with the molar ratio of Fe/Ni further increased, while the plasticity decreases. The yield strength reaches 1,653 MPa at x = 45. The alloy exhibits the best corrosion resistance when x = 35 which is attributed to the dominant FCC phases in the dendritic region. |