AgIn2/Ag2In transformations in an In-49Sn/Ag soldered joint under thermal aging

The interfacial reaction between liquid In-49Sn solders and Ag substrates results in the formation of a thicker Ag₂In intermetallic compound accompanied with the development of a thin AgIn₂ layer. Through further aging of the In-49Sn/Ag soldered specimens at various temperatures ranging from room to 100°C, solid/solid trnasitions between Ag₂In and AgIn₂ intermetallic compounds can be observed. When the temperature drops below 75°C, Ag₂In will react with the In-49Sn solder to form the dominant AgIn₂ phase. Conversely, AgIn₂ is consumed at a higher temperature (e.g., 100°C) when reacting with the Ag substrate to create a now dominant Ag₂In phase. Lastly, the different mechanical, electrical, magnetic, and corrosion behaviors of both intermetallic compounds are respectively made known through direct measurements of the material properties of the individual Ag₂In and AgIn₂ bulk samples.