New dielectric material system of Nd(Mg1/2Ti1/2)O3–CaTiO3 at microwave frequency

The microwave dielectric properties of (1 − x)CaTiO₃–xNd(Mg_1/2Ti_1/2)O₃ (0.1  x  1.0) ceramics prepared by the conventional solid state method have been investigated. The system forms a solid solution throughout the entire compositional range. The dielectric constant decreases from 152 to 27 as x varies from 0.1 to 1.0. In the (1 − x)CaTiO₃–xNd(Mg_1/2Ti_1/2)O₃ system, the microwave dielectric properties can be effectively controlled by varying the x value. At 1400 °C, 0.1CaTiO₃–0.9Nd(Mg_1/2Ti_1/2)O₃ has a dielectric constant (ε_r) of 42, a Q × f value of 35 000 GHz and a temperature coefficient of resonant frequency (τ_f) of −10 ppm/°C. As the content of Nd(Mg_1/2Ti_1/2)O₃ increases, the highest Q × f value of 43 000 GHz for x = 0.9 is achieved at the sintering temperature 1500 °C.