Fine Fe16N2 powder prepared by low-temperature nitridation

α-Fe was prepared by reduction of a fine γ-Fe₂O₃ powder under hydrogen at 500 °C for 8 h. The α-Fe fine powder, about 100 nm in crystallite size, was then nitrided under an ammonia flow at 130 °C for 100 h. X-ray single-phase Fe₁₆N₂ was obtained with a magnetization value of 225 emu/g at room temperature under a magnetic field of 15 kOe. The Mössbauer spectrum at room temperature could be resolved into three sets of hyperfine fields with an average magnetic moment of 2.52 μ_B. An additional paramagnetic component was present in the spectrum with an area ratio of 19%.