Structure study of Bi4Ti3O12 produced via mechanochemically assisted synthesis

Nanosized bismuth titanate was prepared via high-energy ball milling process through mechanically assisted synthesis directly from their oxide mixture of Bi₂O₃ and TiO₂. Only Bi₄Ti₃O₁₂ phase was formed after 3 h of milling time. The excess of 3 wt% Bi₂O₃ added in the initial mixture before milling does not improve significantly the formation of Bi₄Ti₃O₁₂ phase comparing to stoichiometric mixture. The formed phase was amorphized independently of the milling time. The Rietveld analysis was adopted to determine the crystal structure symmetry, amount of amorphous phase, crystallite size and microstrains. With increasing the milling time from 3 to 12 h, the particle size of formed Bi₄Ti₃O₁₂ did not reduced significantly. That was confirmed by SEM and TEM analysis. The particle size was less than 20 nm and show strong tendency to agglomeration. The electron diffraction pattern indicates that Bi₄Ti₃O₁₂ crystalline powder is embedded in an amorphous phase of bismuth titanate. Phase composition and atom ratio in BIT ceramics were determined by X-ray diffraction and EDS analysis.