| Pd-Ba/Ce-Zr-La-Al2O3/堇青石催化剂对甲基丙烯酸尾气的催化燃烧 |
| |
| 引用本文： | 方月萍,郭耘,郭杨龙,卢冠忠,张志刚.Pd-Ba/Ce-Zr-La-Al2O3/堇青石催化剂对甲基丙烯酸尾气的催化燃烧[J].工业催化,2008,16(4):66-70. |
| |
| 作者姓名： | 方月萍 郭耘 郭杨龙 卢冠忠 张志刚 |
| |
| 作者单位： | 结构可控先进功能材料及其制备教育部重点实验室，华东理工大学工业催化研究所，上海 200237 |
| |
| 基金项目： | 国家重点基础研究发展计划(973计划)
,
上海市纳米科技专项基金 |
| |
| 摘 要： | 采用浸渍法制备Pd-Ba/Ce-Zr-La/堇青石催化剂，以甲基丙烯酸尾气为模型，考察Ba的引入对Pd催化剂催化燃烧活性的影响。并用XRD、BET、SEM和TPD等对催化剂进行了表征。研究表明，Ba的引入提高了催化剂的催化活性和热稳定性，经500 ℃焙烧的Pd-Ba/Ce-Zr-La/堇青石催化剂（Pd和Ba质量比为1∶7.5）具有很好的催化活性，起燃温度为130 ℃，完全燃烧温度仅为153 ℃，经1 000 ℃焙烧后，催化剂仍保持较高催化活性。
|
| 关 键 词： | 环境保护工程 Pd-Ba催化剂 甲基丙烯酸尾气 催化燃烧 |
| 文章编号： | 1008-1143(2008)04-0066-05 |
| 修稿时间： | 2007年10月29 |
Catalytic combustion of methacrylic acid tail gas over Pd-Ba/Ce-Zr-La-Al2O3/cordierite monolith catalysts |
| |
| FANG Yueping,GUO Yun,GUO Yanglong,LU Guanzhong,ZHANG Zhigang.Catalytic combustion of methacrylic acid tail gas over Pd-Ba/Ce-Zr-La-Al2O3/cordierite monolith catalysts[J].Industrial Catalysis,2008,16(4):66-70. |
| |
| Authors: | FANG Yueping GUO Yun GUO Yanglong LU Guanzhong ZHANG Zhigang |
| |
| Affiliation: | Lab for Advanced Materials, Research Institute of Industrial Catalysis, East China University of Science and Technology, Shanghai 200237,China |
| |
| Abstract: | Pd-Ba/Ce-Zr-La-Al2O3/cordierite monolith catalysts were prepared by the stepwise impregnation method and characterized by XRD，BET，SEM and TPD. Influence of doping of Ba on behaviors of Pd catalysts for combustion of methacrylic acid tail gas was investigated. The results showed that doping of Ba obviously enhanced catalytic activity and thermal stability of the Pd catalysts. The Pd-Ba/Ce-Zr-La-Al2O3/cordierite monolith catalysts with m(Pd)∶m(Ba) of 1∶7.5 and calcined at 500 ℃ exhibited excellentproperties, with ignition temperature of 130 ℃ and totally combustion temperature of only 153 ℃. The catalyst calcined at 1 000 ℃ still exhibited high activity. |
| |
| Keywords: | Pd-Ba catalyst methacrylic acid tail gas catalytic combustion environmental engineering |