工艺条件对制备三盐基硫酸铅纳米粉体的影响 |
| |
引用本文: | 赵振威,刘俊龙,马铁成.工艺条件对制备三盐基硫酸铅纳米粉体的影响[J].塑料科技,2003(2):20-23. |
| |
作者姓名: | 赵振威 刘俊龙 马铁成 |
| |
作者单位: | 大连轻工业学院材料科学与工程系,辽宁,大连,116034 |
| |
摘 要: | 采用液相沉淀法制备三盐基硫酸铅纳米粉体。在50℃反应条件下,对粉体粒度影响较大的工艺条件进行研究。利用透射电子显微镜对粉体微观形态进行分析。实验结果表明,适当优化制备工艺条件,可以制备出40nm左右的三盐基硫酸铅纳米粉体。
|
关 键 词: | 三盐基硫酸铅 纳米粉体 |
文章编号: | 1005-3360(2003)-02-0020-04 |
Effect of Process Conditions on the Preparation of Tri-base Lead Sulfate Nano-powder |
| |
Abstract: | Tri\|base lead sulfate nano\|powder was prepared by means of liquid phase precipitation method.The process conditions having more effect on the particle size of tri\|base lead sulfate nano\|powder were studied at reaction temperature of 50℃.The micro\|structural morphology nano\|powder were analyzed by using transmission electron microscope.The results showed that the tri\|base lead sulfate nano\|powder with 44nm in diameter could be prepared under the optimal process conditions. |
| |
Keywords: | Tri\|base lead sulfate Nano-powder |