Effects of Al and Zn additions on mechanical properties and precipitation behaviors of Mg-Sn alloy system

For the Mg-Sn-Al alloys, the ultimate strength (UTS) of an extruded Mg-9wt.%Al-2wt.%Sn alloy reached 390 MPa. TEM observation indicated that plate-like Mg₁₇Al₁₂ precipitates having Burgers orientation relationship with the matrix are responsible for the strength. This alloy also exhibits an age hardening behavior: the peak hardness appears after 15-20 h of heat treatment at 473 K. On the other hand, the UTS of the Mg-Mg-Sn-Zn alloys are on the order of 300 MPa. The precipitates in these alloys are composed of the Mg₂Sn and MgZn₂ particles. It was found that these phases often precipitate together, suggesting that the MgZn₂ phase can act as a nucleation sites for Mg₂Sn.