| Abstract: | Presents the investigation of as-cast microstructures of high temperature α + α2 titanium alloys matrix composites reinforced by particles and fabricated using a reaction synthesis method by XRD, OM and SEM
which reveals that the matrix transformed into single phase α2 from two phases α + α2 and reinforcing phases become Ti3A1C and TiC from single phase TiC as C content increases to a critical value, and Ti3AlC precipitates during solidification processing and points out that the norphologies of TiC and Ti3AlC are of short-lath shape and near spherical shape, respectively, and lattice parameters of matrix α2 increase with the increasing of C content, but the lattice parameter of reinforcing phase TiC is lower than standard lattice parameter of TiC due to the C defection in TiC. |