| 微合金化控冷工艺开发HRB500E高强度抗震钢筋 | |
| 引用本文： | 苏灿东,陈伟,陈必胜.微合金化控冷工艺开发HRB500E高强度抗震钢筋[J].钢铁钒钛,2012,33(1):70-75. |
| 作者姓名： | 苏灿东 陈伟 陈必胜 |
| 作者单位： | 1. 武钢集团昆明钢铁股份有限公司技术中心,云南昆明,650302 2. 武钢集团昆明钢铁股份有限公司技术中心,云南昆明650302;昆明理工大学冶金与能源工程学院,云南昆明650093 3. 红河钢铁有限公司,云南蒙自,661111 |
| 基金项目： | 云南省科技计划项目(2009BA008) |
| 摘 要： | 针对红河钢铁有限公司炼钢、轧钢工艺装备,采用微合金化控轧控冷工艺生产HRB500E高强度抗震钢筋,并利用金相显微镜、拉力试验机对钢筋的力学性能、金相显微组织、夹杂物进行检验。结果表明:钢筋强韧性适中,具有较好的抗震性能和低应变时效性;控制钢中Mn含量小于1.55%,Nb含量小于0.025%,控冷终止温度大于680℃,钢筋心部组织为铁素体+珠光体+5%贝氏体,综合性能较佳。 |
| 关 键 词： | HRB500E高强度抗震钢筋 钒氮合金 铌铁 微合金化 控轧控冷 控冷终止温度 贝氏体 |
Development of HRB500E High Strength Anti-seismic Rebars by Microalloying and Controlled Cooling Process |
|
| Su Candong , Chen Wei , Chen Bisheng.Development of HRB500E High Strength Anti-seismic Rebars by Microalloying and Controlled Cooling Process[J].Iron Steel Vanadium Titanium,2012,33(1):70-75. | |
| Authors: | Su Candong Chen Wei Chen Bisheng |
| Affiliation: | 1.Technology Center of WuKun Steel Co.,Ltd.,Kunming 650302,Yunnan,China;2.Faculty of Metallurgical and Energy Engineering,Kunming University of Science and Technology,Kunming 650093,Yunnan,China;3.Honghe Iron and Steel Co.,Ltd.,Mengzhi 661111,Yunnan,China) |
| Abstract: | Considering the existing equipment available in the steelmaking and rolling plants of Honghe Iron and Steel Co.,Ltd.,HRB500E high strength anti-seismic rebars were developed by microalloying,controlled rolling and controlled cooling process and mechanical properties,microstructures,inclusions of rebars so produced were tested by tensile testing machine and metallographic microscopy.The results showed that the rebars exhibited moderate strength & toughness,good anti-seismic performance and low strain aging;Besides,they boosted preferable comprehensive performance,featuring a final temperature after controlled cooling greater than 680 ℃,Mn content less than 1.55%,Nb content less than 0.025%,and core microstructure of ferrite + pearlite +5% bainite. |
| Keywords: | HRB500E high-strength anti-seismic rebar vanadium nitride alloy ferroniobium microalloy controlled rolling and controlled cooling final temperature after controlled cooling bainite |