Synthesis and characterization of epoxy/amine terminated amide‐imide‐imide blends

A new amine terminated amide‐imide (ATAI) was synthesized by the polycondensation reaction of tetrimide dicarboxylic acid containing bulky m‐chloro phenyl pendant with p‐phenylene diamine. The structure of all the prepared compounds were confirmed by FTIR,¹H‐NMR and ¹³C‐NMR techniques. This new diamine was then used to cure epoxy resin namely diglycidyl ester of bisphenol‐A and the cure reaction was studied by Differential scanning calorimetry. The cured blends show better thermal properties. The T_g of the epoxy resin was increased from 134°C to 156°C on addition of 6% of ATAI. The DMA results indicate that the polymer blend with 8% ATAI composition has higher storage modulus compared to 3% and 6% ATAI composition. The polymer blends with 3% and 6% ATAI composition have higher crosslinking density and lower intersegmental and intrasegmental friction coefficients than 8% ATAI composition. In the DMA curves an increase in the peak half‐width was observed with increasing ATAI composition, indicating the possibility of the existence of more than one phase with increasing ATAI concentration. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008