Effect of carbon containing SiNx antireflection coating on the screen‐printed contact and low illumination performance of silicon solar cell

Screen‐printed metal contact formation through a carbon containing antireflection coating was investigated for silicon solar cells by fabricating conventional carbon‐free SiN_x and carbon‐rich SiC_xN_y film. An appreciable difference was found in the average shunt resistance (R_sh), which was about an order of magnitude higher for SiC_xN_y‐coated solar cells relative to the counterpart SiN_x‐coated solar cells. Series resistance (R_s) and fill factor (FF) were comparable for both antireflection coatings but the starting efficiency of SiC_xN_y‐coated cell was ~0·2% lower because of slightly inferior surface passivation. However, SiC_xN_y‐coated solar cells showed less degradation under lower illumination (<1000 W/m²) compared with the SiN_x‐coated cells due to reduced FF degradation under low illumination. Theoretical calculations in this paper support that this is a direct result of high R_sh. Detailed photovoltaic system and cost modeling is performed to quantify the enhanced energy production and the reduced levelized cost of electricity due to higher shunt resistance of the SiC_xN_y‐coated cells. It is shown that R_sh value below 30 Ω (7000 Ω cm² for 239 cm² cell) can lead to appreciable loss in energy production in regions of low solar insolation. Copyright © 2011 John Wiley & Sons, Ltd.