Raman spectra of virgin and damaged graphite edge planes

First-order Raman spectra of virgin and ion irradiated highly oriented pyrolytic graphite were performed along the basal and edge planes. Ion irradiation was performed in the low fluence regime (≈ 10¹²–10¹³ ions cm⁻²) using a 400 keV Ar⁺ beam in order to a introduce controlled amount of defects in the structure. Virgin edge Raman spectra reveal the presence of a 1351 cm⁻¹ structure (D^*) shifted 10 cm⁻¹ away from the disorder induced D-line found upon irradiating or grinding the graphite surface.The 1351 cm⁻¹ D^* structure is then considered as the feature coming from the rupture of the D_6h⁴ space group symmetry. A comparison between D^* and the classical 1360 cm⁻¹ D-line is discussed in terms of induced disorder.