The high-temperature oxidation of Ni-20%Cr alloys containing various oxide dispersions

The oxidation behavior of Ni-20%Cr alloys containing approximately 3 vol.% Y₂O₃, ThO₂, and A1₂O₃ as dispersed particles has been examined in the temperature range 900 to 1200° C in slowly flowing oxygen at 100 Torr. The results show that the oxidation behavior of the Y₂O₃-, ThO₂-, Al₂O₃-, and Ce0₂-containing alloys is very similar and that some anomalies in the behavior of the ThO₂-containing alloy might be explained by the slower rate of chromium diffusion in this coarse-grained alloy. Two Al₂O₃-containing alloys were studied. One with a relatively coarse dispersoid size behaved in a manner analogous to a dispersion-free Ni-30% Cr alloy at 1100°C. The other alloy contained a dispersion of fine Al₂O₃ particles and behaved exactly like the Y₂O₃-containing alloy at 1000 and 1100°C, but at 1200° C oxidized at a faster rate. It has been shown that the adherent scales on dispersion-containing alloys have a stabilized fine grain size, whereas the nonadherent scales on dispersion-free alloys undergo grain growth.This work has been supported by the Naval Air Systems Command under Contract No. N00019-72-C-0190.