Abstract: | MnO_2/activated carbon composite(Mn-ACC) wave absorber was prepared by the reaction between Mn(CH_3COO)_2 and KMnO_4 on activated carbon. Then, a novel cement based composite absorbing coating(CB-CAC) was prepared by adding the Mn-ACC, manganese zinc ferrite and rubber particles into cement. XRD method was used to analyze the reaction products of the Mn-ACC. The tensile bond strength and the wave absorbing properties of the CB-CACs were also tested. The results showed that the crystallinity of MnO_2 formed in the Mn-ACC was poor. Adding Mn-ACC into the CB-CAC led to first increase and then decrease of the tensile bond strength. The tensile bond strength reached 1.89 MPa with 8.51% of the Mn-ACC. The CB-CACs obtained the optimal absorbing properties with the cement, manganese zinc ferrite, Mn-ACC, rubber particles and H_2O mass ratio of 7.5?7.5?1?1?5.5, respectively. The band width of the reflection below-10 dB was up to 8.8 GHz, which accounted for 57.14% of the test band. |