STUDY OF K_(2)O·6TiO_(2) WHISKER REINFORCED AI COMPOSITES FOR THEIR MECHANICAL PROPERTIES AND INTERFACIAL STRUCTURES

A newly developed whisker K_2O 6TiO_2 reinforeed 6061Al composite was prepared bysqueeze casting process.The flexural strength of the composite is 518MPa,and deereasesto 490MPa after T6 treatment.The hardness of the composite also shows the similarchange while T6 treating.The results of HRTEMobservation may explaine this property.change.It was considered that there is a continuous TiO layer at the whisker-matrix inter-face,which is easily to react with the segregated Mg and to form MgTi_2O_4,MgAl_2O_4.Thethickening of TiO layer after T6 treatment is the main reason resulting is strength degra-dation of composite.

STUDY OF K_(2)O·6TiO_(2) WHISKER REINFORCED AI COMPOSITES FOR THEIR MECHANICAL PROPERTIES AND INTERFACIAL STRUCTURES

A newly developed whisker K_(2)O 6TiO_(2) reinforced 6061 Al composite was prepared by squeeze casting process. The flexural strength of the composite is 518MPa, and decreases to 490 M Pa after T6 treatment.The hardness of the composite also shows the similar change while T6 treating. The results of HRTEMobservation may explaine this property change. It was considered that there is a continuous TiO layer at the whisker-matrix interface, which is easily to react with the segregated Mg and to form MgTi_(2)O_(4), MgAl_(2)O_(4). The thickening of TiO layer after T6 treatment is the main reason resulting in strength degradation of composite.