Crystallography of fracture facets in a near-alpha titanium alloy

A faceted initiation site is observed in Ti-6242 alloy for both the cyclic and static-loading test conditions. In this experimental study, the crystallographic orientation of the facets has been determined using the electron backscattered diffraction (EBSD) technique in conjunction with the quantitative tilt fractography in a scanning electron microscope (SEM). Quantitative tilt fractography analysis has been used to determine the spatial orientation of fracture facets. The results indicate that the normal-fatigue (no-dwell) fracture facets are oriented at ∼5 deg with respect to the basal plane; the dwell-fatigue fracture facets are oriented at ∼10 to 15 deg with respect to the basal plane and the static-loading fracture facets are oriented at ∼20 deg with respect to the basal plane. These crystallographic orientation determinations of the fracture facets at the crack-initiation site can be used to obtain an idea about the type of loading that produced them.