Pure and mixed gas permeation study of silica incorporated polyurethane-urea membrane modified by MOCA chain extender

Polyurethane-urea (PUU) nanocomposite membranes have been prepared using various loadings of silica (SiO₂) nanoparticles. A Novel PU was fabricated by a two-step bulk polymerization technique based on polycaprolactone (PCL), hexamethylene diisocyanate (HDI), and diamine chain extender, 4,4-methylenebis(2-chloroaniline) (MOCA). The FTIR spectra indicated that the extent of phase separation reduces with increasing SiO₂ content. The presence of crystal regions in the soft and hard segments was confirmed by DSC and XRD analyses. The obtained results illustrated a decrement in the gases' permeation in the presence of SiO₂ particles. By increasing the filler content up to 15 wt% and pressure of 8 bar, the gas permeation value of the CO₂, O₂, and N₂ decreased 36%, 54%, and 59%, respectively. However, the permselectivity of the CO₂/N₂ and O₂/N₂ increased considerably, 55% and 13% respectively. On the contrary, by raising the temperature, a dramatic augmentation in the permeability of all gases with a simultaneous reduction in the selectivity values of both gas pairs was revealed. Increasing the pressure led to a decrease in the permeability values of all membranes for O₂ and N₂, whereas the permeability for CO₂ increased with the pressure. Nevertheless, the selectivity values for the pair of gases increased (at a pressure of 10 bar, 1.66 and 1.17 times the neat PU for CO₂/N₂ and O₂/N₂, respectively). Furthermore, the permeability of the CO₂, O₂, and N₂ for the mixed gases was smaller than for pure ones at the same gas upstream pressure. Nonetheless, like the pure gas, the selectivity of both pair gases increased.