Hydrogen adsorption on partially truncated and open cage C60 fullerene

C₆₀ buckyball molecules were partially truncated by a controlled oxidation at 400 °C and 2 bar oxygen pressure to create unique pore textures suitable for hydrogen adsorption. Pore textural analysis and density measurement confirmed the success of cage-opening and the creation of pore structures accessible to gas molecules. The specific surface area of the C₆₀ sample were increased from below detection to a measurable value (BET: 85 m²/g). Raman spectral study showed that the three main bands of C₆₀, H_g(1), A_g(1) and A_g(2) remained and significant defects were created after the C₆₀ fullerenes were partially oxidized. XRD and SEM measurements suggested that the C₆₀ fullerenes lost their crystallinity and the crystal surfaces were etched after the oxidation step. Hydrogen adsorption on the C₆₀ fullerenes were measured at three temperatures (77, 143 and 228 K) and hydrogen pressures up to 150 bar. Hydrogen adsorption capacity on C₆₀ fullerenes at 77 K at 120 bar was more than tripled (from 3.9 to 13 wt.%) after the C₆₀ fullerenes were partially oxidized. The average heat of adsorption of hydrogen on the partially oxidized C₆₀ fullerene molecules (2.38 kJ/mol) is within the range of the reported values of heat of adsorption on other porous adsorbents.