| Abstract: | In this study,morphological and microstructural analyses were conducted on net-shaped microcracks appearing on the surface of low-carbon steel manufactured via twin-roll strip casting. The fractograph and microscale distribution of elements in the cracked region were also analyzed. Results revealed that the cracked surfaces were characterized by slight pits,along with inclusions composed of manganese and silicon oxide distributed along both the sides of the cracks. Fractograph analysis revealed that the crack and smooth dendrite surfaces were oxidized. These phenomena indicate that microcracks on the cast strip surface form at the hightemperature stage of the solidification process during twin-roll casting and rolling. Microcracks were present in each region with pits in the cast strip and extended along the dendrite interface because of the combined effects of phasechange stress,thermal stress,mechanical stress,and fractional crystallization during the solidification process. |