高稳定性的SiO_2/HKUST-1复合膜的制备及氢气分离性能
引用本文:逯春晶,王刚,李根,柏明星,黄传鑫. 高稳定性的SiO_2/HKUST-1复合膜的制备及氢气分离性能[J]. 硅酸盐通报, 2019, 38(1): 289-293
作者姓名:逯春晶  王刚  李根  柏明星  黄传鑫
作者单位:东北石油大学提高油气采收率教育部重点实验室,大庆,163318;广东石油化工学院化学工程学院,茂名,525000;吉林大学无机合成与制备化学国家重点实验室,长春,130012
基金项目:黑龙江省青年创新人才培养计划(UNPYSCT-2016082)%石油与天然气工程学科优秀科研人才计划
摘    要:以多孔二氧化硅片为基底,通过接枝硅烷偶联剂制备高稳定性能的SiO_2与HKUST-1复合无机膜。具体做法是将3-氨丙基甲基二甲氧基硅烷拌接枝在SiO_2片上,在SiO_2片表面上接枝的氨基可以参与生长HKUST-1膜,从而制备出大面积连续致密的HKUST-1无机膜。通过X-射线衍射(XRD)、扫描电子显微镜(SEM)、热重分析(TGA)、单组份及混合组分的渗透流量测试装置对得到的复合无机膜的化学结构、表面形貌、热稳定性和气体分离性能进行了表征。结果表明:制备的复合无机膜具有与其晶体一致的晶相,且连续致密,无缺陷;同时具有很好的热稳定性和机械稳定性。气体渗透流量测试结果显示该复合无机膜对氢气具有很好的选择性,可以用来分离和提纯氢气。

关 键 词:SIO2  3-氨丙基三乙氧基硅烷  功能化  无机膜  气体分离

Preparation of High Stability SiO2/HKUST-1 Composite Membrane and Hydrogen Separation Performance
LU Chun-jing,WANG Gang,LI Gen,BAI Ming-xing,HUANG Chuan-xin. Preparation of High Stability SiO2/HKUST-1 Composite Membrane and Hydrogen Separation Performance[J]. Bulletin of the Chinese Ceramic Society, 2019, 38(1): 289-293
Authors:LU Chun-jing  WANG Gang  LI Gen  BAI Ming-xing  HUANG Chuan-xin
Affiliation:(Key Laboratory of Enhanced Oil and Gas Recovery of Ministry of Education in China,Northeast Petroleum University,Daqing 163318,China;School of Chemical Engineering,Guangdong University of Petrochemical Technology,Maoming 525000,China;State Key Laboratory of Inorganic Synthesis&Preparative Chemistry,Jilin University,Changchun 130012,China)
Abstract:SiO2 and HKUST-1 composite inorganic membranes with high stability were prepared based on porous SiO2 substrates.3-aminopropyl methyl dimethoxysilane which was grafting onto SiO2,can be involved in the growth of HKUST-1 film.A large area of continuous and dense HKUST-1 inorganic membrane was prepared.The chemical structure,surface morphology,thermal stability and gas separation performance of the composite inorganic membranes were characterized by X-ray diffraction(XRD),scanning electron microscopy(SEM),thermogravimetric analysis(TGA)and single component and mixed components.The results show that the prepared composite membrane has a crystal phase that is consistent with its crystal,and it is continuous and compact which has no defects,and it has good thermal stability and mechanical stability.The gas permeation rate test shows that the composite inorganic membrane has good selectivity for hydrogen and can be used to separate and purify hydrogen.
Keywords:SiO2  3-aminopropyltriethoxysilane  functionalized  inorganic membrane  gas separation