Ablation resistance of HfC(Si,O)-HfB2(Si,O) composites fabricated by one-step reactive spark plasma sintering |
| |
| Authors: | Wei Hao Na Ni Tianyu Liu Lei Zhou Yao Yao Ling Li Juan Jiang Yinchun Shi Xiaofeng Zhao Ping Xiao |
| |
| Affiliation: | 1. Shanghai Key Laboratory of High-Temperature Materials and Precision Forming, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai, 200240, China;2. Key Lab of Education Ministry for Power Machinery and Engineering, School of Mechanical Engineering, Shanghai Jiao Tong University, Shanghai, 200240, China;3. School of Materials Science and Engineering, Northwestern Polytechnical University, Xi’an, 710072, China |
| |
| Abstract: | A dense HfC(Si, O)-HfB2(Si, O) composite was fabricated by reactive spark plasma sintering using HfC and SiB6 as starting reactants. The best ablation resistance was obtained with the composite fabricated with the addition of 15 vol.% SiB6. After ablation under an oxyacetylene flame for 60 s, the mass and linear ablation rates of this composite were ?0.007 mg cm?2 s?1 and ?0.233 μm s?1, respectively. The negative ablation rates are the result of a slight mass gain/thickness increase, which indicate that the oxidation process was stable and mechanical scouring was limited during ablation. This enhanced ablation resistance was attributed to a unique double-layered oxide formation, which possessed lower oxygen permeability and better mechanical strength. The solid solution nature of the composite and its appropriate phase composition were responsible for the stable oxide structure formation. |
| |
| Keywords: | Hafnium carbide Hafnium diboride Solid solutions Ablation resistance |
| 本文献已被 ScienceDirect 等数据库收录！ |
|