Interfacial microstructure and mechanical properties of ZTA/ZTA joints brazed with Ni-Ti filler metal

The reliable brazing of the ZTA ceramic joints was successfully obtained using Ni-Ti filler metal. The microstructure and mechanical properties of the joints brazed at different temperatures were investigated. During the process of brazing, both Al₂O₃ and ZrO₂ in the ZTA reacted with the Ni-Ti filler, resulting in the formation of the AlNi₂Ti + Ni₂Ti₄O reaction layer adjacent to the ZTA substrate when brazed at 1350 °C for 30 min. NiTi and Ni₃Ti compounds precipitated at the center of brazing seam. When the brazing temperature increased from 1320 °C to 1380 °C, the thickness of AlNi₂Ti + Ni₂Ti₄O layer increased gradually. As the brazing temperature varied from 1400 °C to 1450 °C, TiO was formed adjacent to the ZTA substrate, along with the reduction of Ni₂Ti₄O. AlNi₂Ti distributed at the interface and center of brazing seam. The maximum shear strength of 152 MPa was obtained when brazed at 1420 °C for 30 min.