Synthesis and electrochemical properties of Co-doped Li3V2(PO4)3 cathode materials for lithium-ion batteries

Co-doped Li₃V_2−xCo_x(PO₄)₃/C (x = 0.00, 0.03, 0.05, 0.10, 0.13 or 0.15) compounds were prepared via a solid-state reaction. The Rietveld refinement results indicated that single-phase Li₃V_2−xCo_x(PO₄)₃/C (0 ≤ x ≤ 0.15) with a monoclinic structure was obtained. The X-ray photoelectron spectroscopy (XPS) analysis revealed that the cobalt is present in the +2 oxidation state in Li₃V_2−xCo_x(PO₄)₃. XPS studies also revealed that V⁴⁺ and V³⁺ ions were present in the Co²⁺-doped system. The initial specific capacity decreased as the Co-doping content increased, increasing monotonically with Co content for x > 0.10. Differential capacity curves of Li₃V_2−xCo_x(PO₄)₃/C compounds showed that the voltage peaks associated with the extraction of three Li⁺ ions shifted to higher voltages with an increase in Co content, and when the Co²⁺-doping content reached 0.15, the peak positions returned to those of the unsubstituted Li₃V₂(PO₄)₃ phase. For the Li₃V_1.85Co_0.15(PO₄)₃/C compound, the initial capacity was 163.3 mAh/g (109.4% of the initial capacity of the undoped Li₃V₂(PO₄)₃) and 73.4% capacity retention was observed after 50 cycles at a 0.1 C charge/discharge rate. The doping of Co²⁺into V sites should be favorable for the structural stability of Li₃V_2−xCo_x(PO₄)₃/C compounds and so moderate the volume changes (expansion/contraction) seen during the reversible Li⁺ extraction/insertion, thus resulting in the improvement of cell cycling ability.