Synthesis of spinel LiMn2O4 with manganese carbonate prepared by micro-emulsion method

Micro-spherical particle of MnCO₃ has been successfully synthesized in CTAB-C₈H₁₈-C₄H₉OH-H₂O micro-emulsion system. Mn₂O₃ decomposed from the MnCO₃ is mixed with Li₂CO₃ and sintered at 800 °C for 12 h, and the pure spinel LiMn₂O₄ in sub-micrometer size is obtained. The LiMn₂O₄ has initial discharge specific capacity of 124 mAh g⁻¹ at discharge current of 120 mA g⁻¹ between 3 and 4.2 V, and retains 118 mAh g⁻¹ after 110 cycles. High-rate capability test shows that even at a current density of 16 C, capacity about 103 mAh g⁻¹ is delivered, whose power is 57 times of that at 0.2 C. The capacity loss rate at 55 °C is 0.27% per cycle.