The Use of Large Diameter Monofilament for Improving Peel Resistance of a Brittle High Temperature Adhesive |
| |
Authors: | S Azam J P Sargent |
| |
Affiliation: |
a Sowerby Research Centre, British Aerospace, Bristol, UK |
| |
Abstract: | Peel force measurements as a function of adherend thickness are reported for adhesively bonded specimens based on a cyanate ester resin and aluminium adherends. It has been demonstrated that by incorporating large diameter (0.28mm) PTFE monofilament within the adhesive bond then the peel force and associated fracture energy can be increased significantly over that for specimens based on adhesive alone. Fracture energy measurements are derived for specimens with peeling adherend thickness of up to about 0.6 mm using the 90° peel test. Fracture energies are also derived for peeling of more practically-representative 1.6mm thickness adherends using a single cantilever beam experiment. In-situ photoelasticity and SEM microextensomctry experiments are reported which show the stress fields and displacements associated with the presence of the monofilament. It is believed that the reported increase in measured fracture energy is partly due to the crack pinning effect of the monofilament, and partly due to the monofilament creating a “load shadowed” region between adherend and monofilament which prevents the interfacial crack from propagating between adherend and adhesive. |
| |
Keywords: | High temperature adhesives aluminium peel testing single cantilever and double cantilever beam testing physical modifications fracture energy stress state |
本文献已被 InformaWorld 等数据库收录! |