摘    要:选用KOH为活化剂,利用化学活化法制备炭分子筛膜,考察在热塑性酚醛树脂(PFNR)涂膜液中添加不同质量分数的KOH对炭分子筛膜的影响.结果表明,在炭化过程中,KOH的加入可促进炭分子筛膜孔径的均匀分布,使炭分子筛膜具有发达的孔隙结构.当KOH在PFNR中的添加量从0%增加到4%时,H2的渗透速率由23.68×10-10 mol·m-2·s-1·pa-1提高到28.6×10-10 mol·m-2·s-1·Pa-1;但H2/N2和H2/CH4的分离系数明显下降,分别从471.3下降到147.5、540下降到270.CO2/CH4和O2/N2的分离系数只有轻微下降.

关 键 词:热塑性酚醛树脂  炭分子筛膜  活化  气体分离  KOH

Preparation of carbon molecular sieve membranes by KOH activation for gas separation
ZHANG Xiao-yong , LIU Rui , HU Hao-quan , ZHENG Ming-dong.Preparation of carbon molecular sieve membranes by KOH activation for gas separation[J].New Carbon Materials,2012,27(1):61-66.
Authors:ZHANG Xiao-yong  LIU Rui  HU Hao-quan  ZHENG Ming-dong
Affiliation:1.State Key Laboratory of Fine Chemicals,Institute of Coal Chemical Engineering,Dalian University of Technology,Dalian 116012,China; 2.School of Chemistry and Chemical Engineering,Anhui Key laboratory of Coal Clean Conversion and Utilization, Anhui University of Technology,Ma’anshang 243002,China)
Abstract:Carbon molecular sieve membranes were prepared by the pyrolysis of a mixture containing phenolic novolac resin and KOH.The effects of KOH on the properties of the membranes were investigated.Results showed that membranes with homogeneous pore size distributions and high gas permeation rates can be obtained by controlling the amount of KOH.Their H2 gas permeability increased from 23.68×10-10 to 28.6×10-10 mol · m-2 · s-1 · Pa-1 and H2/N2 and H2/CH4 selectivity decreased from 471.3 to 147.5 and 540 to 270 respectively,while the CO2/CH4 and O2/N2 selectivity changed little with increasing KOH content in the coating solution from 0 to 4 mass%.